JOCE LSAW Welded Steel Pipes (Press Bending)

Longitudinal submerged arc welded is produced by using a single medium and thick plate as the raw material, pressing (rolling) the steel plate in a mold or forming machine into a tube blank, using double-sided submerged arc welding, and expanding the diameter.

Description

The steel plate feed amount can be automatically adjusted according to different steel grades, wall thicknesses, and plate widths. At the same time, the deformation compensation function effectively avoids the adverse effects of mold deformation on the forming and ensures the flatness of the full length of the steel plate during the pressing process. The feeding step is uniform during forming, ensuring the roundness of the tube blank and the flatness of the welding edge. The finished product has a wide range of specifications, and the weld has good toughness, plasticity, uniformity, and compactness. It has the advantages of large pipe diameter, pipe wall thickness, high-pressure resistance, low-temperature resistance, and strong corrosion resistance.

UOE LSAW STEEL PIPES

The UOE mill features the most advanced technology and process, achieves high production efficiency, stable product quality and is equipped with complete inspection equipment. UOE mill adopts U & O forming, the formed pipes are welded inside through five internal welding stations with three wires, and welded outside through four external welding stations with three wires. In accordance with different requirements of the customers, the welded pipe can be expanded either by mechanical or hydrostatic expand to improve dimensional accuracy, and eliminate residual stress.

JOCE LSAW PIPES(PRESS BENDING)

This is large diameter longitudinal submerged arc welded (LSAW) pipe production line in China. The mill adopts progressive bending process, featuring evenly distributed forming stress, high uniformity of dimension, infinite sizes variation&wide prouct range, and high flexibility, etc.

Standard

Grade

Chemical Composition(max)%

Mechanical Properties(min)

C

Mn

Si

S

P

Yield Strength(Mpa)

Tensile Strength(Mpa)

GB/T700-2006

A

0.22

1.4

0.35

0.050

0.045

235

370

B

0.2

1.4

0.35

0.045

0.045

235

370

C

0.17

1.4

0.35

0.040

0.040

235

370

D

0.17

1.4

0.35

0.035

0.035

235

370

GB/T1591-2009

A

0.2

1.7

0.5

0.035

0.035

345

470

B

0.2

1.7

0.5

0.030

0.030

345

470

C

0.2

1.7

0.5

0.030

0.030

345

470

BS En10025

S235JR

0.17

1.4

-

0.035

0.035

235

360

S275JR

0.21

1.5

-

0.035

0.035

275

410

S355JR

0.24

1.6

-

0.035

0.035

355

470

DIN 17100

ST37-2

0.2

-

-

0.050

0.050

225

340

ST44-2

0.21

-

-

0.050

0.050

265

410

ST52-3

0.2

1.6

0.55

0.040

0.040

345

490

JIS G3101

SS400

-

-

-

0.050

0.050

235

400

SS490

-

-

-

0.050

0.050

275

490

API 5L PSL1

A

0.22

0.9

-

0.03

0.03

210

335

B

0.26

1.2

-

0.03

0.03

245

415

X42

0.26

1.3

-

0.03

0.03

290

415

X46

0.26

1.4

-

0.03

0.03

320

435

X52

0.26

1.4

-

0.03

0.03

360

460

X56

0.26

1.1

-

0.03

0.03

390

490

X60

0.26

1.4

-

0.03

0.03

415

520

X65

0.26

1.45

-

0.03

0.03

450

535

X70

0.26

1.65

-

0.03

0.03

585

570